ASP® 2030 Powder Metallurgy High-Speed Steel

Material available in round and flat sections

ASP® 2030 is a cobalt grade for high performance cutting and cold work tools.

Applications

Physical Properties

Temperature	20°C	400°C	600°C
Density g/cm3	8.1	7.9	7.9
Modulus of elasticity kN/mm²	240	214	192
Thermal expansion ratio per °C	-	11.8x10 -6	12.3x10 -6
Thermal conductivity W/m°C	24	28	27
Speciﬁc heat J/kg°C	420	510	600

4-Point Bend Strength

Hardening temperature in °C

Original dimension Ø 6 mm
Tempering 3 x 1 hour at 560°C
Dimension of test piece Ø 4.7 mm

Rmb = Ultimate bend strength in kN/mm²

Reb = Bend yield strength in kN/mm²

Tot. work = Total work in Nm

Heat Treatment

Soft annealing in a protective atmosphere at 850-900°C for 3 hours, followed by slow cooling at 10°C/h down to 700°C, then air cooling.
Stress-relieving at 600°C to 700°C for approximately 2 hours, slow cooling down to 500°C.
Hardening in a protective atmosphere with preheating in 2 steps at 450-500°C and 850-900°C and austenitizing at a temperature suitable for chosen working hardness. Cooling down to 40-50°C.
Tempering at 560°C three times for at least 1 hour each time. Cooling to room temperature < 25°C between tempering.

Surface Treatment

The steel grade is a perfect substrate material for PVD coating. If nitriding is requested, a small diffusion zone is recommended but avoid compound and oxidized layers.

Guidelines For Hardening

Tempering temperature in °C

Hardness after hardening, quenching and tempering 3 x 1 hour